Composition:
| Item |
Result |
| Cement G (lbs) |
110 |
| FL-19 (lbs) |
0/55 |
| Fresh/Water |
48-7 |
| Slurry Weight (Pcf) |
118 |
| Pressure (Psi) |
ATM |
| Temprature (F) |
185 |
| Initial Mixing |
Good |
| Viscosity Ini. (Cps) |
8 |
| Viscosity after 60 Min (Cps) |
13 |
| Viscosity after 240 Min (Cps) |
19 |
| Pumping Time (Min) |
450 |
| Thickening Time (Min) |
440 |
| Comp. Str. 8 hr in 100 f (Psi) |
865 |
| Comp. Str. 8 hr in 140 f (Psi) |
2240 |
| Water Loss ml. |
2.25 |
| Thickening Time Minutes
(According To API Spec.) |
107 |
|
.
|
Item |
TEST CONDITIONS |
RESULTS |
| W/C |
TEMP |
PRES |
AFTER |
| RATIO |
OF |
PSI |
24 HRS. |
| Compressive Strength, Psi |
46 % |
80-170 |
3000 |
>1900 Psi |
| Thickening Time, Minutes (According
To API Schedule) |
46 % |
80-113 |
3870 |
110 Minutes |
| Maximum Viscosity During
First 60 Minutes Posises |
46 % |
80-113 |
3870 |
<30 CPS |
Sieve Residue Percent
On Sieve ASTM 20
On Sieve ASTM 200 |
|
0.3 Gr.
9.92 Gr. |
| Free Water Content |
ml. / 250 ml.
Of Slurry |
<2.5 ml. |
| Specific Surface |
cm 2 / Gram |
2950 |
|